Article_5_3_2
DENTAL MATERIALS
Original Article
THE EFFECT OF CERAMIC LIGHT SCATTERING ON AN INHOMOGENEOUS BEAM PROFILE
Jean-François Roulet1a* , Marwah Majid Khudhair1b, Chiayi Shen1c
1
Department for Restorative Dental Sciences, Center for Dental Biomaterials, College of Dentistry, University of Florida, 1395 Center Drive, Gainesville FL
32610, USA
a
Dr med dent, Dr hc, Professor, Director of Center for Dental Biomaterials
b
DDS, Preceptor
c
PhD, Professor
ABSTRACT DOI: 10.25241/stomaeduj.2018.5(3).art.2
Aim: The study aimed to measure light scattering of a broad spectrum light curing unit (LCU) as OPEN ACCESS This is an
influenced by ceramic type, shade and thickness as well as exposure distance and LCU’s position. Open Access article under the CC
BY-NC 4.0 license.
Methodology: A broad spectrum LED LCU (ASCENT OL5) was mounted above a spectrometer Peer-Reviewed Article
(MARC Resin Calibrator, Blue, Light Analytics) at exposure distances of 1.0, 1.5 or 2.5 mm. The
position of the center of the head was aligned with the spectrophotometer’s sensor and then Citation: Roulet J-F, Khudhair MM,
Shen C. The effect of ceramic light
moved in 1 mm increments in the X-Y plane, while concomitantly recording the irradiance. The scattering on an inhomogeneous beam
profile. Stoma Edu J. 2018;5(3):155-
process was repeated with lithium disilicate and leucite glass ceramic slabs of similar thicknesses. 160
The loss in irradiance related to the value measured at center position was analyzed by means
Academic Editor: Nicoleta Ilie,
of linear regressions and multiple ANOVA analysis. Dipl-Eng, PhD, Professor, Ludwig-
Results: The regressions showed a good fit (90% - 99%). Moving away from the center showed Maximilians-Universität München,
München, Germany
decreased irradiance. Values of slope obtained were divided by their respective intercept to
eliminate the influence of the irradiance measured at the center. Two three-way ANOVA’s were Received: June 19, 2018
Revised: July 04, 2018
performed. One examined the influence of ceramic slab, direction and translucency/shade. It Acccepted: July 27, 2018
shows only the direction of measurement exhibited significant influence (p < 0.0001) on the Published: August 01, 2018
mean normalized slope values. The other one examined the influence of ceramic slab, direction *Corresponding author: Professor
Jean-François Roulet, DMD, PhD, Dr hc
and slab thickness. It shows the mean normalized slope values are significantly influenced by Center for Dental Biomaterials, College
the direction of measurement and the slab thickness (p < 0.0001). Values of the slopes indicated of Dentistry, University of Florida
Room D9-26, 1395 Center Drive, PO
the ceramic scattering effect of the light. Thicker samples showed more scattering. Box 100415 Gainesville, FL 32610-
Conclusion: The ceramic types, translucency/ shade had no significant effect on the light 0415, USA
Tel: +1 352 273 5850; Fax: +1 352 846
scattering. The thicker the ceramic the less irradiance changes were found indicating that the 1643, e-mail: jroulet@dental.ufl.edu
ceramics were scattering the light and thus slightly alleviating the effect of the inhomogeneous Copyright: © 2018 the Editorial
beam profile. Council for the Stomatology Edu
Keywords: light curing, beam profile, glass ceramics, light scattering. Journal.
1. Introduction restoration such as optical behavior, crystalline
Bonded ceramic restorations have been used in structure, grain size, defects, intrinsic porosity, thickness
dentistry for many decades and the first application and shade [10]. After passing 0.5 mm thick ceramic, the
was the resin bonded ceramic veneer [1,2]. A few years irradiance of the light reaching the resin-based luting
later, resin bonded ceramic inlays were tested first in agent would be reduced by approximately 75% [7].
vitro [3] and later in vivo [4]. In order to have enough In order to fulfill its function as luting agent, the resin-
time for the cementation process, clinicians prefer light- based luting agent must be adequately polymerized.
cure resin-based composites (RBC), which usually have This depends on its composition, e.g. the resin mix,
a lower viscosity (luting agents) to facilitate the process the refractive index of the filler, the filler size and
of bonding veneers to teeth [5]. For inlays, which are size distribution, pigment, and the photo initiators
usually thicker, dual-cure resin-based luting agents are used [11,12]. Using microhardness measurements,
preferred [5], because it is not clear if the blue light may for Variolink Estetic (Ivoclar Vivadent) the minimum
penetrate the ceramic sufficiently to cure the resin- energy required for adequate curing was found to be
based luting agent. A clinical study has shown that approximately 5 J/cm2 [13].
after 12 years of observation, glass ceramic inlays and Modern broad spectrum LED light curing units
onlays (Empress, Ivoclar Vivadent) luted with dual-cure (LCU), use different types of LEDs, emitting light with
resin-based luting agent showed significantly fewer different wavelengths (violet light (380 – 420 nm)
bulk fractures than those luted with a light-cured RBC and blue light (420 – 495 nm) [14,15]. Therefore, they
(Tetric, Ivoclar Vivadent) [6]. Today we know that glass are able to activate different types of photoinitiators
ceramics (leucite and lithium disilicate ceramics) are [16]. Historically, the most used photoinitiator is
absorbing the blue light to a considerable amount champhorquinone (CQ) which has an absoption peak
[7-9]. The degree of light attenuation by overlying at 470 nm and requires a tertiary amine as co-initiator,
ceramics depends on the characteristics of the ceramic which reacts with the activated CQ to create a free
Stomatology Edu Journal 155
THE EFFECT OF CERAMIC LIGHT SCATTERING ON AN
INHOMOGENEOUS BEAM PROFILE
radical used for the polymerization of the resin [17].
Original Article These amines, unfortunately, create a yellowing effect
on the material over time [17]. Recently manufacturers
started to use alternative photoinitiators, such as
phenylbis-(2,4,6-trimethylbenzoyl)-phosphine-oxide
(TPO) [18] or bis-(4methoxybenzoyl)diethyl-germane
(Ivocerin) [19,20]. These photoinitiators are much more
effective than the combination of CQ and tertiary amine,
but have absorption peaks below 410 nm (TPO) or 430
nm (Ivocerin), thus requiring broad band LCUs which
usually have two different LEDs, (blue and violet light).
However, these LED LCUs show more or less pronounced
inhomogeneity of the beam profiles [21-24]. This
means that not every point on an irradiated surface
gets exposed to the same level of irradiation from the
Figure 1. Measuring points as related to the position within the light exit
different wavelengths, especially in depth [25-27].
window. Blue cross = geometrical center of the light exiting window.
Since ceramics scatter the light because its direction is Orange circles =“WEST”, Light blue circles =“EAST”, Purple circles =“North”
changed at the grain boundaries, one can assume that and green circles =“SOUTH”(From Roulet et al 2018).
the local irradiances may vary less, once the light has Table 1. The ceramics used and their translucency/shade.
passed through the ceramic, thus moving the beam
profile more towards homogeneity. Furthermore, Material Shade and Translucency
since the light is absorbed and scattered more with the IPS Empress
A1LT B1LT C2LT D3LT B3HT C2HT
thicker ceramic, this should affect the homogeneity of CAD
the beam profile as well. IPS e.max
The objective of this study was to measure the beam A1LT B1LT C2LT D3LT B3HT C2HT
CAD
homogeneity of an LCU with known inhomogeneous
beam profile after the light had passed ceramic slices Table 2. The ratio of slope to the intercept of linear regression for all
of different thickness. ceramics.
The null hypothesis tested is that (a) the ceramic has no
Empress e.max
effect on the beam profile and (b) the thickness of the Direction
Translucency
/Shade
ceramic has no effect on the beam profile as well. 1.0
mm
1.5
mm
2.5
mm
1.0
mm
1.5
mm
2.5
mm
HTB3 0.135 0.130 0.115 0.135 0.130 0.115
2. Materials and Methods HTC2 0.129 0.123 0.126 0.129 0.123 0.126
A broad spectrum LED LCU (ASCENT OL5, CAO Group LTA1 0.130 0.136 0.126 0.130 0.136 0.126
South Jordan, UT, USA) was attached to an x-y-z East
positioning device mounted on an optical bench LTB1 0.132 0.123 0.123 0.132 0.123 0.123
in order to standardize the positioning of the light LTC2 0.134 0.128 0.123 0.134 0.128 0.123
beam centered above the cosine corrector light signal LTD3 0.130 0.134 0.119 0.130 0.134 0.119
collector of a spectrometer (MARC® Resin Calibrator,
Blue light Analytics, Halifax, Canada) with the handle HTB3 0.169 0.165 0.141 0.169 0.165 0.141
towards the right side (“EAST”, Figure 1) at an exposure HTC2 0.163 0.148 0.129 0.163 0.148 0.129
distance of 1.0, 1.5 or 2.5 mm. The diameter of the LTA1 0.129 0.193 0.149 0.129 0.193 0.149
cosine corrector was 3.9 mm. Using the translation West
stage, the position of the geometrical center of the LTB1 0.158 0.145 0.142 0.158 0.145 0.142
LCU was first aligned with that of the cosine corrector LTC2 0.172 0.169 0.146 0.172 0.169 0.146
and then moved in 1-mm steps in the x-y plane (“EAST”
LTD3 0.159 0.164 0.157 0.159 0.164 0.157
– “WEST” and “NORTH” – “SOUTH”) (Fig. 1). At each
position, the irradiance was measured in triplicates. HTB3 0.141 0.140 0.120 0.141 0.140 0.120
The process was repeated with ceramic slabs of 1.0, 1.5 HTC2 0.146 0.132 0.132 0.146 0.132 0.132
or 2.5 mm thickness while applying the LCU directly
LTA1 0.156 0.141 0.141 0.156 0.141 0.141
on the ceramic slabs. The ceramics used and their North
translucency/shade are listed in Table 1. LTB1 0.145 0.142 0.132 0.145 0.142 0.132
IPS Empress CAD slabs were used as cut from blocks LTC2 0.144 0.137 0.129 0.144 0.137 0.129
with a diamond saw (Isomet 100, Buhler, Lake Bluff,
LTD3 0.149 0.143 0.137 0.149 0.143 0.137
USA), IPS e.max CAD slabs were cut from blocks and
processed according to manufacturer’s instructions HTB3 0.159 0.154 0.137 0.159 0.154 0.137
in an oven (Programat P-500, Ivoclar Vivadent), under HTC2 0.168 0.148 0.143 0.168 0.148 0.143
vacuum, using the following parameters: heating rate
of 90°C/min up to 820 °C, holding time 0:10 min, then LTA1 0.170 0.120 0.124 0.170 0.120 0.124
South
heating rate of 30°C/min up to 840°C hold for 7:00 min, LTB1 0.168 0.143 0.140 0.168 0.143 0.140
followed by long-term cooling. LTC2 0.167 0.142 0.150 0.167 0.142 0.150
The irradiance was assessed at each condition
described above and related to the highest irradiance LTD3 0.162 0.162 0.147 0.162 0.162 0.147
156 Stoma Edu J. 2018;5(3):155-160. http://www.stomaeduj.com
THE EFFECT OF CERAMIC LIGHT SCATTERING ON AN
INHOMOGENEOUS BEAM PROFILE
Original Article
Table 3. The ratio of slope to the intercept of linear regression (pooled shades and translucencies).
No ceramic slabs Empress e.max
Direction
1.0 mm 1.5 mm 2.5 mm 1.0 mm 1.5 mm 2.5 mm 1.0 mm 1.5 mm 2.5 mm
East 0.117 0.122 0.091 0.132±0.002 0.129±0.005 0.122±0.004 0.132±0.020 0.124±0.014 0.116±0.015
West 0.190 0.175 0.141 0.158±0.015 0.164±0.017 0.144±0.009 0.193±0.009 0.187±0.009 0.168±0.009
North 0.163 0.161 0.156 0.147±0.005 0.139±0.004 0.132±0.007 0.155±0.009 0.151±0.008 0.141±0.006
South 0.187 0.172 0.186 0.166±0.004 0.145±0.014 0.140±0.009 0.139±0.015 0.130±0.005 0.114±0.010
(a) (a)
(b) (b)
Figure 2. Effect of disk thickness on irradiance change in E-W direction Figure 3. Irradiance change from center in E-W direction (a) and N-S
(a) and N-S direction (b). direction (b).
value which was identified in the present study when normalized slope values with a unit of mm-1. Although
positioning the LCU directly and centered on the decreasing irradiance with offset distance yielded
sensor. The percentage of irradiance loss was statistical negative value of the slope; to avoid potential confusion of
analyzed by means of linear regression for each negative sign in the text absolute value of the normalized
material, shade, thickness and direction. The effect of slope is used (Table 2).
vertical position (distance between LCU and bottom Two three-way ANOVA’s were performed. One examined
of ceramic or sensor surface), horizontal position or the influence of ceramic slab, direction and translucency/
off-set (X-Y plane), glass ceramic type, thickness and shade. It shows only the direction of measurement
shade on the irradiance were analyzed using multiple exhibited significant influence (p < 0.0001) on the mean
ANOVA’s (SAS 9.4, Cary, NC, USA). normalized slope values. The other one examined the
influence of ceramic slab, direction and slab thickness. It
shows the mean normalized slope values are significantly
3. Results influenced by the direction of measurement and the slab
The numerical data show that there is a linear relationship thickness (p < 0.0001). The mean normalized slope value
between the irradiance measured by the MARC unit is in the decreasing order of 1.0, 1.5 and 2.5 mm. For the
and the offset distance from the center, excluding effect of direction of measurement, the mean normalized
the irradiance value at the center. A total of 144 linear slope value is in the decreasing order of North, West, South
regressions (SAS 9.4) were performed from a combination and East. It means the inhomogeneity of the light curing
of two ceramic, four directions, three slab thicknesses and depends on the device and the thickness of the ceramic
six translucency/shade of each ceramic. The degree of fit slabs. The optical characteristic of the ceramic would have
was in general greater than 90% with the majority in the no influence on the inhomogeneity as determined by
99% range. The value of intercept of linear regression is MARC. Figure 2 shows the values of irradiance with respect
the calculated irradiance at the center and can influence to the offset distance and direction of measurements for
the values of the slope. To normalize the irradiance at the each thickness of the two ceramics.
center, each value of slope was divided by the respective The mean and standard deviation of normalized slope
value of intercept of the linear regression resulting values by offset distance and slab thickness are pooled
Stomatology Edu Journal 157
THE EFFECT OF CERAMIC LIGHT SCATTERING ON AN
INHOMOGENEOUS BEAM PROFILE
together for each ceramic in Table 3 along with those reduction relative to the offset distance. A flatter slope
Original Article when no ceramic slabs were present. The values of no determined from the same experimental configuration
ceramic slabs were means of taken from a previous study but with the presence of ceramic slabs would mean that
[28]. Figure 3 shows the mean irradiance values measured increased scattering of the light has occurred. As seen in
at each location. The values in the figure are means of all Fig. 3, the absolute irradiance values without ceramic were
thickness and translucency/shade for both ceramics. substantially higher than those with ceramic interposition.
Therefore, for direct comparisons, the slopes must be
normalized as described in Materials and Methods. The
4. Discussion ANOVA’s showed that there were no significant differences
The LCU used in this study was selected on purpose with respect to the ceramic materials and translucency/
because it is known to have a quite inhomogeneous shade; however, highly significant differences for the
beam profile as shown in a previous study [28]. The position (design of LCU) and thickness of the ceramic.
objective of this study was to show the effect of ceramics It is known to clinicians that the translucency and the
on the inhomogeneity of the beam profile. shade have a high impact on the aesthetical outcome
Therefore, it makes sense to use an LCU, where this of a restoration. This is the reason why ceramics are not
characteristic is to be expected. As shown in the previous only produced in different shades, but also in different
study, the blue range the LCU used was so dominant translucencies. Therefore, it is interesting to see that the
(irradiance: blue 1088 mW/cm2 vs violet 71 mW/cm2) shades/translucencies have little effect of scattering the
[28], that the observed effects may be mainly for the light in the blue or purple range. This confirms that yellow
blue light portion only. However, two factors need to be colors are more important to reach good esthetics with
considered, that may influence the outcome. First, it is restorations of teeth.
known that the violet light is scattered differently from In Table 2 where the data of all ceramics tested are
the blue light by ceramic, which is seen by the different displayed, the slopes with thick slabs are always lower,
rate of attenuation [29]. Second, one should remember which means that there is a light scattering effect by the
that the sensitivity of photo initiators sensible in the violet thickness of the ceramic; the thicker the ceramic the more
range is much higher than the one of camphorquinone light scattering. The same is visible in Table 3, where the
for the blue light. Thus, despite the less amount of violet ceramic shades and translucencies were pooled.
light reaching the resin-based composite, due to the Based on the outcome of the ANOVA’s, the ceramic had
better efficiency, the initiation of the polymerization no effect on the beam profile, which can also be seen
is effectively enough to cure the RBC [30], which may in Tab. 3. Therefore, the first null hypothesis must be
influence the degree of conversion of an RBC at least accepted. However, one must note that the ceramic had
under thin layers of the ceramic [29]. a strong effect when one looks at the attenuation of the
In the present study, the LCU was laterally moved in a light, which was not the topic of the present investigation.
controlled way in the X- and Y-direction of a coordinated The second null hypothesis can be rejected, since thicker
system. This creates a decrease in the irradiance as a ceramic slabs showed more scattering of the light.
function of the offset from the center value, which can
be determined as a slope, as seen in Figs 2 and 3, and Tab.
2, which is the expression of the inhomogeneity of the 5. Conclusion
beam profile. The thicker the ceramic the fewer irradiance changes
With the method used (controlled lateral movements), were found as a function of the position indicating that
the inhomogeneity of the beam could be roughly the ceramics were scattering the light and thus slightly
reproduced. However, the cosine corrector light signal alleviating the effect of the inhomogeneous beam profile.
collector used has a diameter of 3.9 mm, which limits the
precision. It is suggested for future measurements to use a
smaller sensor diameter. Author contributions
The ceramics used for the present study (Empress and JFR: Idea, experimental design, wrote the manuscript.
IPS e.max) were chosen because they are sufficiently CS: Performed data analysis, substantially contributed
translucent for resin-bonded restorations (inlays, onlays, to writing manuscript. MMK: Performed spectrometer
veneers and crowns) where light curing of the resin experiment.
bonded luting material may be an option [31,32].
Therefore, the scattering behavior of the blue (and violet)
light is important if the beam profile is inhomogeneous). Acknowledgement
It is known that the irradiance at the target surface The authors have no conflicts of interest. This research
received is a function of the exposure distance [21]. did not receive any specific grant from funding agencies
Therefore, the decrease in irradiance reported in Fig. 2 is in the public, commercial, or not-for-profit sectors. The
not only due to the increased thickness of the ceramic but authors declare that the research was conducted in the
also to the increasing distance from the sensor to the light absence of any commercial or financial relationship that
exciting window of the LCU. Figure 3 confirms the fact could be construed as a potential conflict of interest.
that interposing ceramics in the light beam attenuates a
substantive amount of light irradiance [7,33].
The decrease in irradiance as the measuring point moves References
farther away from the center is due to the design of the 1. Simonsen RJ, Calamia JR. Tensile bond strengths of etched
porcelain. J Dent Res. 1983; 62 (2 Suppl): 297, Abstract #1099.
LCU and representative for its beam profile. A steeper 2. Calamia JR. Etched porcelain facial veneers: a new treatment
slope (higher value) means a greater rate of irradiance modality based on scientific and clinical evidence. N Y J Dent.
158 Stoma Edu J. 2018;5(3): 155-160. http://www.stomaeduj.com
THE EFFECT OF CERAMIC LIGHT SCATTERING ON AN
INHOMOGENEOUS BEAM PROFILE
1983;53(6):255-259. jdent.2015.08.015.
[PubMed] Google Scholar (227) Scopus (91) [Full text links] [PubMed] Google Scholar (41) Scopus (23)
Original Article
3. Geppert W, Roulet J-F. In vitro marginal integrity of MOD Dicor 18. Neumann MG, Schmitt CC, Ferreira GC, Corrêa IC. The initiating
inlays luted with adhesive techniques. IADR DMG Microfilm, Publ. radical yields and the efficiency of polymerization for various
No. 48. 1986. dental photoinitiators excited by different light curing units. Dent
Google Scholar (21) Mater. 2006;22(6): 576-584.doi: 10.1016/j.dental.2005.06.006.
4. Herder SM, Roulet JF. [Marginal adaptation of bonded Dicor inlays [Full text links] [PubMed] Google Scholar (150) Scopus (90)
in vivo]. [Article in German]. Dtsch Zahnärztl Z. 1988;43(8):904- 19. Moszner N, Zeuner F, Lamparth I, Fischer UK. Benzoylgermanium
908. derivatives as novel visible light photoinitiators for dental
[PubMed] Google Scholar (24) Scopus (10) composites. Macromol Mater Eng. 2009;294(12):877-886. doi:
5. Pegoraro TA, da Silva NR, Carvalho RM. Cements for use in 10.1002/mame.200900181.
esthetic dentistry. Dent Clin North Am. 2007;51(2):453-471, x. doi: Google Scholar (56) Scopus (48)
10.1016/j.cden.2007.02.003. 20. Moszner N,.Fischer UK, Salz U, Liska R. Burtscher P, Zeuner F,
[Full text links] [PubMed] Google Scholar (222) Scopus (72) Ganster B, Gruber H. Polymerisierbare Zusammensetzungen mit
6. Frankenberger R, Taschner M, Garcia-Godoy F, et al. Leucite- Acylgermaniumverbindungen als Initiatoren. US-Patent 7,605,
reinforced glass ceramic inlays and onlays after 12 years. J Adhes 190 B2 (20.10.2009), EP-Patent 1,905,415 B1 (01.07.2009), Ivoclar
Dent. 2008; 10(5):393-398. Vivadent AG.
[PubMed] Google Scholar (122) Scopus (67) 21. Megremis S, Ong V, Lukic H, Shepelak H. An ADA laboratory
7. Shen C, Roulet JF. Dispersion of curing light irradiance through evaluation of light-emitting diode curing lights. J Am Dent Assoc.
new CAD/CAM prosthetic materials. A paper presented at: 43rd 2014;145(11):1164-1166. doi: 10.14219/jada.2014.97.
Annual Meeting & Exhibition of the AADR; 2014: Charlotte, NC, [Full text links] [PubMed] Google Scholar (3)
March 21st, Abstr No. 721. 22. Shortall AC, Felix CJ, Watts DC. Robust spectrometer-based
8. Moreno MBP, Costa AR, Rueggeberg FA, et al. Correr AB, Sinhoreti methods for characterizing radiant exitance of dental LED light
MAC, Ambrosano GMB, Consani S, Correr-Sobrinho L. Effect curing units. Dent Mater. 2015;31(4):339-350. doi: 10.1016/j.
of ceramic interposition and post-activation times on Knoop dental.2015.02.012.
hardness of different shades of resin cement. Braz Dent J. [Full text links] [PubMed] Google Scholar (13) Scopus (10)
2018;29(1):76-81. doi: 10.1590/0103-6440201801635. 23. Price RB, Rueggeberg FA, Labrie D, Felix C. Irradiance uniformity
[Full text links] [PubMed] Google Scholar (0) Scopus (0) and distribution from dental light curing units. J Esthet Restor
9. Oliveira DCRS, Rocha MG, Souza-Junior EJ, et al. The effect of Dent. 2010;22(2): 86-101. doi: 10.1111/ j.1708-8240.2010.00319.x.
shade and curing mode on cure efficiency of dual cured resin [Full text links] [PubMed] Google Scholar (60) Scopus (39)
cements. Braz Dent Sci. 2016;19(3):59-64. doi: 10.14295/bds.2016. 24. Michaud PL, Price RB, Labrie D, et al. Localized irradiance
v19i3.1265. distribution found in dental light curing units. J Dent.
Google Scholar (0) 2014;42(2):129-139. doi: 10.1016/j.jdent.2013.11.014.
10. Sharma G, Wu WC, Dalal EN, Celik MU. Mathematical [Full text links] [PubMed] Google Scholar (60) Scopus (36)
discontinuities in CIEDE2000 color difference computations. 25. Rocha MR, de Oliveira D, Correa IC, et al. Light-emitting diode
The Twelfth Color Imaging Conference: Color Science and beam and spectral output influence on the degree of conversion
Engineering Systems, Technologies, Applications, CIC 2004, of bulk fill composites. Oper Dent. 2017; 42(4):418-427. doi:
Scottsdale, AZ, USA, November 9-12, 2004 : 334-339. 10.2341/16-164-L.
Google Scholar (14) Scopus (5) [Full text links] [PubMed] Google Scholar (4) Scopus (0)
11. Hirt T. Ivocerin - a milestone in composite technology. Report No. 26. de Oliveira D, Rocha MG, Correa IC, et al. The effect of combining
19. Schaan, Liechtenstein: Ivoclar Vivadent AG; 2013. photoinitiator systems on the color and curing profile of resin-
12. Todd JC, Wanner M. The future of composite technology. Tetric based composites. Dent Mater. 2016;32(10):1209-1217. doi:
Evoceram Bulkfill - Scientific Documentation. Liechtenstein: 10.1016/j.dental.2016.06.010.
Ivoclar Vivadent Schaan AG; 2014. [Full text links] [PubMed] Google Scholar (10) Scopus (6)
13. Goetz NE, Shen C, Roulet JF. Energy requirements for curing 27. Roulet J-F, Rocha MG, Shen C, et al. Beam profile characterization
light activated cements trough CAD/CAM materials. J Dental. of a dental light curing unit using a spectrometer-based method.
2014;30(Suppl. 1):e3. doi: 10.1016/j.dental.2014.08.006. Stoma Edu J. 2018;5(2):84-91. doi: 10.25241/stomaeduj.2018.5(2).
Google Scholar (0) art.1.
14. André CB, Nima G, Sebold M, et al. Stability of the light output, 28. Castellanos ME, Sinhoreti MAC, Oliveira DCRS, et al. Effect of
oral cavity tip accessibility in posterior region and emission thickness of ceramic veneers on color stability and bond strength
spectrum of light-curing units. Oper Dent. 2018;43(4):398-407. of resin cements containing alternative photoinitiators. J Adhes
doi: 10.2341/17-033-L. Dent. 2018;20: submitted.
[Full text links] [PubMed] Google Scholar (0) Scopus (0) 29. Harlow JE, Sullivan B, Shortall AC, et al. Characterizing the output
15. Jandt KD, Mills RW. A brief history of LED photopolymerization. settings of dental curing lights. J Dent. 2016;44:20-26. doi:
Dent Mater. 2013;29(6):605-617. doi: 10.1016/j.dental.2013.02.003. 10.1016/j.jdent.2015.10.019.
[Full text links] [PubMed] Google Scholar (124) Scopus (74) [Full text links] [PubMed] Google Scholar (17) Scopus (15)
16. Price RB, Ferracane JL, Shortall AC. Light-Curing Units: a review of 30. Bühler-Zemp P, Völkel T, Fischer K. IPS Empress CAD - Scientific
what we need to know. J Dent Res. 2015;94(9):1179 –1186. doi: Documentation. Schaan Liechtenstein: Ivoclar Vivadent AG; 2011.
10.1177/0022034515594786. 31. Fischer K, Bühler-Zemp P, Völkel T. IPS e.max CAD - Scientific
[Full text links] [PubMed] Google Scholar (51) Scopus (28) Documentation. Schaan Liechtenstein: Ivoclar Vivadent AG; 2011.
17. de Oliveira DC, Rocha MG, Gatti A, et al. Effect of different 32. Roulet J-F, Shen C. Light curing cements through indirect
photoinitiators and reducing agents on cure efficiency and restorative materials. Paper presented at: 92nd General Session &
color stability of resin based composites using different LED Exhibition of the IADR, IADR Africa/Middle East Region Meeting;
wavelengths. J Dent. 2015;43(12):1565-1572. doi: 10.1016/j. June 26th 2014; Capetown South Africa. Abstr No: 538.
Jean-François ROULET
DDS, DMD, PhD, Dr hc, Prof hc, Professor, Chair
Department of Restorative Dental Sciences, Center for Dental Biomaterials
College of Dentistry, University of Florida
Gainesville, FL, USA
CV
Jean-François Roulet, DDS, Dr med dent, PhD, is the former chair and current professor of the Department of Restorative Dental
Sciences at the University of Florida. Professor Roulet is author/coauthor of more than 180 papers, edited/contributed to 27
textbooks and mentored more than 150 theses. He is a renowned international lecturer with over 800 appearances to date. Dr.
Roulet is a member of many professional organizations, has won numerous awards, and holds four patents. He is editor of the
Prophylaxe Impuls and Stomatology Edu Journal. His areas of interest include minimally invasive dentistry, dental materials (ie,
composites and ceramics), adhesive dentistry, esthetic dentistry, and application concepts in preventive dentistry.
Stomatology Edu Journal 159
THE EFFECT OF CERAMIC LIGHT SCATTERING ON AN
INHOMOGENEOUS BEAM PROFILE
Questions
Original Article
1. Why are amine free resin-based composites preferred to bond veneers?
qa. They allow for a longer working time;
qb. Tertiary amines used in combination with campherquinone tend to discolor over time;
qc. Tertiary amines and campherquinone require a broadband light curing unit;
qd. Amine free resin-based composites provide a stronger bond.
2. Which ceramics were used for the experiment?
qa. Leucite reinforced ceramic and lithium disilicate ceramic;
qb. Translucent Zirconium oxide ceramic;
qc. Feldspathic ceramic;
qd. None of the above.
3. The results were analyzed with:
qa. ANOVA and Wilcoxon test;
qb. ANOVA and t-test;
qc. ANOVA and Kruskal Walls Test;
qd. ANOVA and linear regression.
4. Which was the main outcome of the experiment?
qa. Ceramic color, shade and type had a significant effect on the scattering of light;
qb. Ceramic did not alter the irradiance;
qc. All of the above;
qd. The thicker the ceramic, the more light-scattering occurred.
https://www.gnydm.com/
160 Stoma Edu J. 2018;5(3): 155-160. http://www.stomaeduj.com